Nonwoven thermal bonding interlining is made by adding hot melt adhesive fibers to polyester fibers, melting the hot melt adhesive, and bonding the polyester fibers through a hot rolling process to make a nonwoven backing, then coated with LDPE or EVA adhesive powder according to demand. The non-woven base fabric produced has a softer feel and uses very few chemical additives, making it more environmentally friendly and widely used for various types of garment lining or temporary bonding.

Detailed Product Specifications and Parameters:

Detailed specifications: 12G LDPE or EVA adhesive powder on 25G hot rolled process backing, generally using a dusting of flat glue sizing process.

Composition:

100% polyester chemical fiber

Grammage range:

Base fabric: 25G; Coating: 12G

Width range:

within 2 meters

Color:

white, black

MOQ:

5000m

Feeling hardness:

regular feeling

Packing quantity:

according to customer requirements

Packing material:

PE transparent plastic bag

Loading quantity:

20GT/40HQ

Customs code:

5603911090; 5603921090; 5603931090.

Glue powder:

LDPE/EVA

LDPE pressing temperature:

130-140 degrees

Pressure:

2-2.5kg/cm2

Time:

12-15S

EVA pressing temperature:

100-110 degrees

Pressure:

0.1-0.5kg/cm2

Time:

10-12S

Features:

25G regular weight hot rolled backing, medium thickness, soft-touch, even and flat, also can produce different weight and width according to customers' requirements.

Nonwoven thermal bonding interlining can be coated with LDPE or EVA adhesive powder according to customers' requirements, and the gluing process is flexible, it can be directly dusted with powder or hot-pressed into the flat adhesive.

No need to add chemical additives in the production process, the product is environmentally friendly and free of odor and harmful substances.

The simple production process, high yield, low cost, high-cost performance, and wide range of applicable garments.

Introduction To The Production Process Of Backing Fabric:

Backing production: The polyester staple fiber, or and other fibers through the open cotton process to fully break up the fiber, dot fusing mixed, and then after carding, laying the network, by hot rolling stick hot roll forming to complete the production of the base fabric. Glue powder coating: The hot melt adhesive resin is ground into certain particle size of hot melt the adhesive powder, then the hot melt adhesive powder is scattered on the top surface of the backing as evenly as possible, then the powder is hot molten in the drying room, flat fusing on the top surface of the backing and then cooled, or the adhesive powder is flattened by hot pressing roller, the finished product is hot rolled nonwoven interlining.